Use of hydrolysis prior to the chemical and thermomechanical modification of rice starch: alternative to traditional modification treatments
Rice starch isolated (NS), was subjected to chemical and thermomechanical modification with previous hydrolysis (MHS) and without previous hydrolysis (MS) to be evaluated on main starch properties as degree of substitution (DS), color, water absorption and solubility index (WAI, WSI), viscosity, tex...
محفوظ في:
| المؤلفون الرئيسيون: | , , , , , , , , , |
|---|---|
| التنسيق: | Online |
| اللغة: | eng |
| منشور في: |
Universidad de Sonora
2021
|
| الوصول للمادة أونلاين: | https://biotecnia.unison.mx/index.php/biotecnia/article/view/1296 |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| الملخص: | Rice starch isolated (NS), was subjected to chemical and thermomechanical modification with previous hydrolysis (MHS) and without previous hydrolysis (MS) to be evaluated on main starch properties as degree of substitution (DS), color, water absorption and solubility index (WAI, WSI), viscosity, texture, thermal properties (differential scanning calorimetry DSC) and structural properties (infrared-IR, Xray-Rx analysis, and relative crystallinity index-ICR). The modified starches were compared to native starch (NS). The DS obtained in both starches was within the range allowed by the FDA for its safety use as food ingredient (0.01-0.2). The modification showed an increase in WAI and WSI values, being WAI value higher in MS (4.80) and WSI value higher in MHS (32.06). The viscosity of retrogradation showed a significant decrease (P<0.05) in both starches (HMS 0.013 and MS 5.613), obtaining gels with greater stability, however, the hardness of starch gels decreased (60 %) while the adhesiveness decreased only in MS (66 %). The crystallinity index (ICR) of the modified starches increased with regard to the native starch indicating a depolymerization of the molecule due to the modification. The presence of the acetyl group in the starch molecule was observed in the signals between 1650 to 1744 cm-1 confirming the esterification. The starches showed a high potential for its application as edible coatings and as wall material for microencapsulation. |
|---|